Do irrigation solutions influence the bond interface between glass fiber posts and dentin?

Abstract The aim of this study was to evaluate the push-out bond strength and interface permeability of glass-fiber posts in different regions of post space (cervical, middle, and apical) submitted to different irrigation solutions. Ninety single-rooted human teeth were submitted to endodontic treatment and divided into five groups, according to irrigation solutions: distilled water, 5.25% NaOCl, 25% polyacrylic acid, 2% chlorhexidine, and 23 ppm Ag NP dispersion. Each group was divided in 3 subgroups (n=6) according to cementation: SBU: Adper Scotchbond Universal + RelyX ARC; U200: RelyX U200; MCE: MaxCem Elite. Bond strength and sealing ability were measured in different areas of post space. The data was subjected to ANOVA and Fisher's test (a=0,05). The silver nanoparticle solution showed highest bond strength values and lowest interface permeability in all thirds analyzed for SBU group. In the U200 group, the highest bond strength values were found for sodium hypochlorite solution, with significant difference between this solution and polyacrylic acid. A decrease in bond strength values in cervical to apical direction was found for MCE group and the same behavior were found for others groups. Regarding interface permeability, use of silver nanoparticle solution resulted in lower values in cervical and apical thirds. There was a decrease in bond strength in cervical to apical direction. Different irrigation solutions and intraradicular depth influenced the bond strength and interface permeability of adhesive material to dentin substrate. Silver nanoparticle solution can effectively be used as an irrigation agent in post space prior to fiber post cementation process.

Resumo O objetivo deste trabalho foi avaliar a resistência de união e permeabilidade da interface de pinos de fibra de vidro nos diferentes terços da dentina intrarradicular (cervical, médio e apical) submetidos a diferentes agentes irrigantes. Noventa dentes unirradiculares humanos foram submetidos ao tratamento endodôntico e foram divididos em cinco grupos de acordo com os agentes irrigantes: água destilada, hipoclorito de sódio 5,25%, ácido poliacrílico 25%, clorexidina 2% e dispersão de nanopartícula de prata à 23 ppm. Os grupos foram divididos em 3 subgrupos (n=6) de acordo com a técnica adotada para cimentação adesiva dos pinos de fibra de vidro: Grupo SBU: sistema adesivo ScotchbondTM Universal + cimento resinoso RelyX ARC; Grupo U200: cimento resinoso autoadesivo RelyX U200; Grupo MCE: cimento resinoso autoadesivo Maxcem Elite. A resistência de união e a permeabilidade da interface foram mensurados em diferentes áreas da dentina intrarradicular. Os dados foram submetidos a ANOVA e teste de Fisher (a=0,05). Amostras representativas foram levadas à microscopia eletrônica de varredura. A solução de nanopartícula de prata apresentou os maiores valores de resistência de união em todos os terços analisados para o grupo SBU. No grupo U200, os maiores valores foram encontrados para a solução de hipoclorito de sódio, com diferença para o ácido poliacrílico. Observou-se uma diminuição nos valores de resistência de união na direção cérvico-apical para o grupo MCE e o mesmo comportamento foram encontrados para os demais grupos. Com relação a permeabilidade da interface, o uso da solução de nanopartícula de prata resultou em menores valores nos terços cervical e apical. Houve diminuição dos valores de resistência de união no sentido cérvico-apical. As diferentes soluções irrigantes, bem como a profundidade intrarradicular influenciaram a resistência de união e permeabilidade da interface dos materiais adesivos ao substrato dentinário. A nanopartícula de prata pode ser utilizada como agente irrigador do conduto radicular previamente à cimentação de pinos de fibra de vidro.

Comparative Evaluation of Radicular Push-out Bond Strength of EndoSequence BC, MTA FillApex, Apexit Plus and AH Plus Sealers as Affected by the Modified Plunger: Base Orifice Size Relation

Background: Sealers are universally used along with gutta-percha to obturate the root canals in three dimensions. Push-out bond strength is considered appropriate to measure the adhesion capacity of sealers. Aim: To compare the bond strength of recently introduced bioceramic sealer with commonly used sealers and to evaluate the effect of plunger: base orifice size ratio on push-out bond strength. Methods:One hundred mandibular premolars with single canals were decoronated and instrumented up to master apical file F3 Protaper. Specimens were randomly divided into four groups (n=25) based on the sealer used: Group 1-EndoSequence BC Sealer, Group 2-MTA FillApex sealer, Group3-Apexit Plus sealer & Group 4-AH Plus sealer and obturated using cold lateral compaction technique. After two weeks, 1±0.1mm thick slice of each radicular third of specimens was subjected to push-out testing with modified and standardised plunger: base orifice size ratio for each slice and bond strength calculated. Subsequently the slices were observed under stereomicroscope for failure mode analysis. Results: Results showed that AH Plus sealer had the highest overall bond strength followed by EndoSequence BC sealer and MTA FillApex while as Apexit Plus had lowest bond strength. Bond strength of all sealers reduced from coronal to apical direction except in EndoSequence BC sealer which showed better strength in critical apical third. Higher bond strength values were obtained due to modified relation of plunger with base orifice size. Conclusion: Bond strength of all sealers tested except EndoSequence BC reduces in apical direction and is impacted by plunger: base orifice size ratio.

Retention of fiber posts in different dentin regions: An in vitro study.

Aim: The aim of this study was to evaluate the influence of different regions of dentin within the post space on the retention of fiber posts. Materials and Methods: Ten human incisors with straight roots were selected for this study. Endodontic treatment of the specimens was done. The post spaces were created immediately after obturation and the posts were luted with dual-cure resin cement. Approximately 2.5-mm-thick sections were made from the coronal, middle, and apical thirds of the post space and thus we had three groups: Group I: Cervical, Group II: Middle, Group III: Apical. The specimens were tested on a universal testing machine. Statistical analysis was done using the unpaired Student's t-test and one-way ANOVA test. Result: The best push-out strength was obtained with the apical sections (14.69±0.298 MPa), followed by the middle (10.66±0.34 MPa) and cervical sections (9.73±0.42 MPa). Conclusion: highest pust out strengths were obtained in apical sections followed by middle and coronal.